2% Secant Modulus, MD (ASTM D882) in MPa (psi)
|
900 (131000)
|
|
2% Secant Modulus, TD (ASTM D882) in MPa (psi)
|
900 (131000)
|
|
Bottles and Drums Use
|
Household Industrial Chemicals (HIC) / Agriculture Bottles, Personal Care
|
|
Density Range
|
.961+
|
|
ESCR-Environmental Stress Crack Resistance (100% IGEPAL)
|
> 280 hr
|
|
Fabrication Method
|
Blow Molding
|
|
Functionality
|
Mechanical Performance
|
|
Tensile Elongation at Break, MD
|
1000 %
|
|
Tensile Elongation at Break, TD
|
1000 %
|
|
Tensile Strength Break, MD (ASTM D638) in MPa (psi)
|
36 (5220)
|
|
Tensile Strength Break, TD (ASTM D638) in MPa (psi)
|
36 (5220)
|
|
Tensile Strength Yield, MD (ASTM D638) in MPa (psi)
|
28 (4060)
|
|
Tensile Strength Yield, TD (ASTM D638) in MPa (psi)
|
28 (4060)
|