Dart Drop Impact (ASTM D1709A) in grams (lbs)
|
100 g
|
|
Elmendorf Tear Strength, MD (ASTM D1922) in grams (lbs)
|
560 g
|
|
Elmendorf Tear Strength, TD (ASTM D1922) in grams (lbs)
|
470 g
|
|
Fabrication Method
|
Blown Film Extrusion, Cast Film Extrusion
|
|
Functionality
|
Mechanical Performance
|
|
Melting Point, DSC (Dow Method) in °C(°F)
|
111 (232)
|
|
Puncture Resistance (Dow Method) in joules/cm3 (lbs/in3)
|
2.81 J/cm3 (34 ft lb/in3)
|
|
Tensile Elongation at Break, MD
|
520 %
|
|
Tensile Elongation at Break, TD
|
720 %
|
|
Tensile Strength Break, MD (ASTM D882) in MPa (psi)
|
24.8 (3600)
|
|
Tensile Strength Break, TD (ASTM D882) in MPa (psi)
|
20.8 (3010)
|
|
Tensile Strength Yield, MD (ASTM D882) in MPa (psi)
|
12 (1740)
|
|
Tensile Strength Yield, TD (ASTM D882) in MPa (psi)
|
12.3 (1780)
|
|
Vicat Softening Point in °C(°F)
|
92.2 (198)
|