Dart Drop Impact (ASTM D1709A) in grams (lbs)
|
Blown Film - 87 g
|
|
Elmendorf Tear Strength, MD (ASTM D1922) in grams (lbs)
|
Blown Film - 450 g
|
|
Elmendorf Tear Strength, TD (ASTM D1922) in grams (lbs)
|
Blown Film - 430 g
|
|
Fabrication Method
|
Blown Film Extrusion, Cast Film Extrusion
|
|
Functionality
|
Optical Performance, Processing
|
|
Haze (ASTM D1003)
|
Blown Film - 5.7 %
|
|
Melting Point, DSC (Dow Method) in °C(°F)
|
113 (235)
|
|
Puncture Resistance (Dow Method) in joules/cm3 (lbs/in3)
|
Blown Film - 3.47 J/cm3 (42 ft lb/in3)
|
|
Tensile Elongation at Break, MD
|
Blown Film - 780 %
|
|
Tensile Elongation at Break, TD
|
Blown Film - 580 %
|
|
Tensile Strength Break, MD (ASTM D882) in MPa (psi)
|
Blown Film - 23.4 (3400)
|
|
Tensile Strength Break, TD (ASTM D882) in MPa (psi)
|
Blown Film - 20.6 (2990)
|
|
Tensile Strength Yield, MD (ASTM D882) in MPa (psi)
|
Blown film - 12.5 (1810)
|
|
Tensile Strength Yield, TD (ASTM D882) in MPa (psi)
|
Blown Film - 12.7 (1840)
|
|
Vicat Softening Point in °C(°F)
|
97.2 (207)
|