Dart Drop Impact (ASTM D1709A) in grams (lbs)
|
130
|
|
Elmendorf Tear Strength, MD (ASTM D1922) in grams (lbs)
|
110
|
|
Elmendorf Tear Strength, TD (ASTM D1922) in grams (lbs)
|
610
|
|
Fabrication Method
|
Blown Film Extrusion, Cast Film Extrusion
|
|
Functionality
|
Mechanical Performance
|
|
Melting Point, DSC (Dow Method) in °C(°F)
|
121 (250)
|
|
Puncture Resistance (Dow Method) in joules/cm3 (lbs/in3)
|
2.44 (29.5)
|
|
Tensile Elongation at Break, MD
|
150 %
|
|
Tensile Elongation at Break, TD
|
580 %
|
|
Tensile Strength Break, MD (ASTM D882) in MPa (psi)
|
18.0 (2610)
|
|
Tensile Strength Break, TD (ASTM D882) in MPa (psi)
|
18.6 (2700)
|
|
Tensile Strength Yield, MD (ASTM D882) in MPa (psi)
|
10.6 (1540)
|
|
Tensile Strength Yield, TD (ASTM D882) in MPa (psi)
|
10.5 (1520)
|
|
Vicat Softening Point in °C(°F)
|
99.5 (211)
|