Elmendorf Tear Strength, MD (ASTM D1922) in grams (lbs)
|
590 g
|
|
Elmendorf Tear Strength, TD (ASTM D1922) in grams (lbs)
|
1300 g
|
|
Fabrication Method
|
Blow Molding, Blown Film Extrusion, Oriented (Machine Direction), Sheet Extrusion
|
|
Functionality
|
Mechanical Performance, Sealant (non-peelable)
|
|
Heat Seal Initiation Temp in °C(°F)
|
60 (140)
|
|
Melt Index ((g/10min @190°C/2.16 kg) (ASTM D1238))
|
2
|
|
Melting Point, DSC (Dow Method) in °C(°F)
|
82.2 (180)
|
|
Tensile Elongation at Break, MD
|
690 (ASTM D638) %
|
|
Tensile Elongation at Break, TD
|
690 (ASTM D638) %
|
|
Tensile Strength Break, MD (ASTM D882) in MPa (psi)
|
29.5 (4280)
|
|
Tensile Strength Break, TD (ASTM D882) in MPa (psi)
|
26.3 (3810)
|
|
Tensile Strength Yield, MD (ASTM D882) in MPa (psi)
|
10.7 (1550)
|
|
Tensile Strength Yield, TD (ASTM D882) in MPa (psi)
|
10.1 (1460)
|
|
Vicat Softening Point in °C(°F)
|
63 (145)
|