Fabrication Method
|
Compounding and Blending
|
|
Functionality
|
Sealant (non-peelable)
|
|
Melting Point, DSC (Dow Method) in °C(°F)
|
70 (158)
|
|
Tensile Elongation at Break, MD
|
190 %
|
|
Tensile Elongation at Break, TD
|
190 %
|
|
Tensile Strength Break, MD (ASTM D882) in MPa (psi)
|
1.76 (255) ASTM D638 (not at break)
|
|
Tensile Strength Break, TD (ASTM D882) in MPa (psi)
|
1.76 (255) ASTM D638 (not at break)
|
|
Tensile Strength Yield, MD (ASTM D882) in MPa (psi)
|
1.76 (255) ASTM D638 (not at yield)
|
|
Tensile Strength Yield, TD (ASTM D882) in MPa (psi)
|
1.76 (255) ASTM D638 (not at yield)
|
|
Viscosity (350°F)
|
17000 cP
|