物性

key.properties.Title

Density 0.96 g/cm3
Melt Index (g/10min @190°C/2.16 kg (ASTM D1238)) 8

app.properties.Title

Anti-block No
Slip No

typical.properties.Title

2% Secant Modulus, MD (ASTM D882) in MPa (psi) 1110 (160000) ASTM D638
2% Secant Modulus, TD (ASTM D882) in MPa (psi) 1110 (160000) ASTM D638
Density Range .951-.960
ESCR-Environmental Stress Crack Resistance (100% IGEPAL) 3 hr
Fabrication Method Injection Molding
Functionality Mechanical Performance
Structure Type Monolayer, Multilayer
Tensile Elongation at Break, MD 670 %
Tensile Elongation at Break, TD 670 %
Tensile Strength Break, MD (ASTM D638) in MPa (psi) 17 (2470)
Tensile Strength Break, TD (ASTM D638) in MPa (psi) 17 (2470)
Tensile Strength Yield, MD (ASTM D638) in MPa (psi) 29 (4200)
Tensile Strength Yield, TD (ASTM D638) in MPa (psi) 29 (4200)