物性
key.properties.Title |
|
|---|---|
| Density | 0.918 g/cm3 |
| Melt Index (g/10min @190°C/2.16 kg (ASTM D1238)) | 8 |
app.properties.Title |
|
|---|---|
| Anti-block | No |
| Closure Type | Fitments, Hinges, Pull Tabs |
| Slip | No |
product.use.formulating.properties.Title |
|
|---|---|
| Type | Breathable Blown Film |
typical.properties.Title |
|
|---|---|
| 2% Secant Modulus, MD (ASTM D882) in MPa (psi) | 234 (36000) (ASTM D790B) |
| 2% Secant Modulus, TD (ASTM D882) in MPa (psi) | 234 (36000) (ASTM D790B) |
| Fabrication Method | Extrusion Coating and Lamination, Injection Molding |
| Functionality | Mechanical Performance |
| Impact Strength in MPa (psi) | 273 kJ/m2 (130 ft lb/in2) ASTM D1822 |
| Melting Point, DSC (Dow Method) in °C(°F) | 107 (224) |
| Tensile Elongation at Break, MD | 500 (ASTM D638) % |
| Tensile Elongation at Break, TD | 500 (ASTM D638) % |
| Tensile Strength Break, MD (ASTM D882) in MPa (psi) | 9.65 (1400) (ASTM D638) |
| Tensile Strength Break, TD (ASTM D882) in MPa (psi) | 9.65 (1400) (ASTM D638) |
| Tensile Strength Yield, MD (ASTM D882) in MPa (psi) | 8.27 (1200) (ASTM D638) |
| Tensile Strength Yield, TD (ASTM D882) in MPa (psi) | 8.27 (1200) (ASTM D638) |
| Vicat Softening Point in °C(°F) | 87.8 (190) |