物性
key.properties.Title |
|
|---|---|
| Density | 0.94 g/cm3 |
| Melt Index ((g/10min @190°C/21.6 kg) (ASTM D1238)) | 17 |
| Melt Index (g/10min @190°C/2.16 kg (ASTM D1238)) | .74 |
app.properties.Title |
|
|---|---|
| Anti-block | No |
| Slip | No |
typical.properties.Title |
|
|---|---|
| 2% Secant Modulus, MD (ASTM D882) in MPa (psi) | 827 (120000) |
| ESCR-Environmental Stress Crack Resistance (100% IGEPAL) | >3000 hr - 100˚C (212˚F) |
| Fabrication Method | Blown Film Extrusion, Pipe Extrusion |
| Functionality | Mechanical Performance |
| Impact Strength in MPa (psi) | 590 J/m (11 ft-lb/in) - Notched Izod Impact (23˚C (73˚F)) |
| Tensile Elongation at Break, MD | 800 % |
| Tensile Strength Break, MD (ASTM D882) in MPa (psi) | 33.0 (4790) |
| Tensile Strength Yield, MD (ASTM D882) in MPa (psi) | 21.0 (3040) |