物性
key.properties.Title |
|
|---|---|
| Density | 0.939 g/cm3 |
| Melt Index (g/10min @190°C/2.16 kg (ASTM D1238)) | 0.38 |
app.properties.Title |
|
|---|---|
| Anti-block | No |
| Slip | No |
typical.properties.Title |
|
|---|---|
| 2% Secant Modulus, MD (ASTM D882) in MPa (psi) | 800 (116000) |
| ESCR-Environmental Stress Crack Resistance (10% IGEPAL) | >3000 hr - 50˚C (122˚F) |
| Fabrication Method | Blown Film Extrusion |
| Functionality | Mechanical Performance |
| Impact Strength in MPa (psi) | 82 J/m (1.5 ft-lb/in) - Notched Izod Impact (23˚C (73˚F)) |
| Melt Index (g/10min @190°C/5.0 kg (ASTM D1238)) | 0.38 |
| Tensile Elongation at Break, MD | >800 % |
| Tensile Strength Break, MD (ASTM D882) in MPa (psi) | 30.0 (4350) |
| Tensile Strength Yield, MD (ASTM D882) in MPa (psi) | 19.0 (2760) |
| Vicat Softening Point in °C(°F) | 118 (244) |