Fabrication Method
|
Pipe Extrusion
|
|
Functionality
|
Mechanical Performance
|
|
Melt Index (g/10min @190°C/5.0 kg (ASTM D1238))
|
0.38
|
|
Puncture Resistance (Dow Method) in joules/cm3 (lbs/in3)
|
4.96 (60)
|
|
Tensile Elongation at Break, MD
|
380 %
|
|
Tensile Elongation at Break, TD
|
670 %
|
|
Tensile Strength Break, MD (ASTM D638) in MPa (psi)
|
77.9 (11300) ASTM D882
|
|
Tensile Strength Break, TD (ASTM D638) in MPa (psi)
|
42 (6090) ASTM D882
|
|
Tensile Strength Yield, MD (ASTM D638) in MPa (psi)
|
40 (5800) ASTM D882
|
|
Tensile Strength Yield, TD (ASTM D638) in MPa (psi)
|
30 (4350) ASTM D882
|