2% Secant Modulus, MD (ASTM D882) in MPa (psi)
|
800 (116000)
|
|
ESCR-Environmental Stress Crack Resistance (10% IGEPAL)
|
>3000 hr - 50˚C (122˚F)
|
|
Fabrication Method
|
Blown Film Extrusion
|
|
Functionality
|
Mechanical Performance
|
|
Impact Strength in MPa (psi)
|
82 J/m (1.5 ft-lb/in) - Notched Izod Impact (23˚C (73˚F))
|
|
Melt Index (g/10min @190°C/5.0 kg (ASTM D1238))
|
0.38
|
|
Tensile Elongation at Break, MD
|
>800 %
|
|
Tensile Strength Break, MD (ASTM D882) in MPa (psi)
|
30.0 (4350)
|
|
Tensile Strength Yield, MD (ASTM D882) in MPa (psi)
|
19.0 (2760)
|
|
Vicat Softening Point in °C(°F)
|
118 (244)
|