REVOLOOP™ 70-LD NA Recycled Plastics Resins

What is REVOLOOP™ 70-LD NA Recycled Plastics Resins?

The resin is designed with 70% recycled content for use in secondary and tertiary packaging, particularly in collation shrink applications or film formulations that can benefit from LDPE properties. This high performance PCR rich resin is designed to provide improved homogeneity and consistency over other film-based PCR resin offerings. Produced using circular feedstocks made from mixed plastic waste. Certified on a mass balance basis by the International Sustainability & Carbon Certification (ISCC).

Uses

Collation shrink
Secondary and tertiary packaging

Benefits

Improved quality and consistency
High percentage of PCR (flexibility)
Continuous product improvement
Reduced carbon footprint

Properties

key.properties.Title
Density	0.93 g/cm3
Melt Index (g/10min @190°C/2.16 kg (ASTM D1238))	0.35

app.properties.Title
Anti-block	No
Slip	No

typical.properties.Title
Dart Drop Impact (ASTM D1709A) in grams (lbs)	130
Elmendorf Tear Strength, MD (ASTM D1922) in grams (lbs)	110
Elmendorf Tear Strength, TD (ASTM D1922) in grams (lbs)	610
Fabrication Method	Blown Film Extrusion, Cast Film Extrusion
Functionality	Mechanical Performance
Gloss (45 degree)	28
Haze (ASTM D1003)	36 %
Melting Point, DSC (Dow Method) in °C(°F)	121 (250)
Puncture Resistance (Dow Method) in joules/cm3 (lbs/in3)	2.44 (29.5)
Tensile Elongation at Break, MD	150 %
Tensile Elongation at Break, TD	580 %
Tensile Strength Break, MD (ASTM D882) in MPa (psi)	18.0 (2610)
Tensile Strength Break, TD (ASTM D882) in MPa (psi)	18.6 (2700)
Tensile Strength Yield, MD (ASTM D882) in MPa (psi)	10.6 (1540)
Tensile Strength Yield, TD (ASTM D882) in MPa (psi)	10.5 (1520)
Vicat Softening Point in °C(°F)	99.5 (211)

REVOLOOP™ 70-LD NA Recycled Plastics Resins

What is REVOLOOP™ 70-LD NA Recycled Plastics Resins?

Uses

Benefits

Properties

key.properties.Title

app.properties.Title

typical.properties.Title

RESOURCES

EDUCATION

CORPORATE

LEGAL